| Reny® 1022HS | |||
| Polyarylamide | |||
| 50% Glass Fiber | |||
| Product Description | |||
| Reny® 1022HS is a Polyarylamide (PARA) material filled with 50% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Primary attribute of Reny® 1022HS: Flame Rated. | |||
| General | |||
| UL Yellow Card 2 | E41179-231738 | ||
| E41179-231739 | |||
| Filler / Reinforcement | Glass Fiber, 50% Filler by Weight | ||
| Processing Method | Injection Molding | ||
| Physical | Dry | Conditioned | Unit | Test Method |
| Density | 1.66 | -- | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (275°C/2.16 kg) | 6 | -- | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (275°C/2.16 kg) | 3 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.34 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 0.1 | -- | % | |
| Equilibrium, 23°C, 50% RH | 0.87 | -- | % | |
| Mechanical | Dry | Conditioned | Unit | Test Method |
| Tensile Modulus | 21900 | 21000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 236 | 233 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.5 | 1.6 | % | ISO 527-2 |
| Flexural Modulus | 19100 | 19000 | MPa | ISO 178 |
| Flexural Stress | 384 | 326 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
| Charpy Notched Impact Strength (23°C) | 12 | 12 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 61 | 40 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 245 | -- | °C | ISO 75-2/A |
| CLTE | ISO 11359-2 | |||
| Flow | 1.00E-05 | -- | cm/cm/°C | |
| Transverse | 4.00E-05 | -- | cm/cm/°C | |
| Electrical | Dry | Conditioned | Unit | Test Method |
| Surface Resistivity | 5.00E+15 | -- | ohms | IEC 60093 |
| Volume Resistivity | 1.00E+16 | -- | ohms·cm | IEC 60093 |
| Electric Strength | IEC 60243-1 | |||
| 1.00 mm | 33 | -- | kV/mm | |
| 2.00 mm | 24 | -- | kV/mm | |
| Relative Permittivity (1 MHz) | 4.7 | -- | IEC 60250 | |
| Dissipation Factor (1 MHz) | 9.00E-03 | -- | IEC 60250 | |
| Flammability | Dry | Conditioned | Unit | Test Method |
| Flame Rating | HB | -- | UL 94 | |
| Injection | Dry | Unit | ||
| Drying Temperature | ||||
| A | 120 | °C | ||
| B | 80 | °C | ||
| Drying Time | ||||
| A | > 3.0 | hr | ||
| B | > 12 | hr | ||
| Rear Temperature | 280 | °C | ||
| Middle Temperature | 285 | °C | ||
| Front Temperature | 290 | °C | ||
| Nozzle Temperature | 290 | °C | ||
| Mold Temperature | 80.0 to 140 | °C | ||
| Injection Pressure | 20.0 to 150 | MPa | ||
| Injection Rate | Moderate-Fast | |||
| Screw Speed | 60 to 150 | rpm |