PARA Reny® 1322

2018-09-05

Reny® 1322
Polyarylamide
50% Glass Fiber
Product Description
Reny® 1322 is a Polyarylamide (PARA) material filled with 50% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding.

Important attributes of Reny® 1322 are:

Flame Rated

Impact Resistant

General
Filler / Reinforcement	Glass Fiber, 50% Filler by Weight

Features	High Impact Resistance

Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Density	1.6	g/cm³	ISO 1183
Molding Shrinkage	0.4	%
Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	18100	MPa	ISO 527-2
Tensile Stress (Break)	245	MPa	ISO 527-2
Tensile Strain (Break)	2.1	%	ISO 527-2
Flexural Modulus	16500	MPa	ISO 178
Flexural Stress	387	MPa	ISO 178
Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	17	kJ/m²	ISO 179
Charpy Unnotched Impact Strength (23°C)	94	kJ/m²	ISO 179
Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	225	°C	ISO 75-2/A
Flammability	Nominal Value		Test Method
Flame Rating			UL 94
--	HB
1.60 mm	HB
Injection	Nominal Value	Unit
Drying Temperature
A	120	°C
B	80	°C
Drying Time
A	> 3.0	hr
B	> 12	hr
Rear Temperature	270	°C
Middle Temperature	275	°C
Front Temperature	280	°C
Nozzle Temperature	280	°C
Mold Temperature	120 to 140	°C
Injection Pressure	20.0 to 150	MPa
Injection Rate	Moderate-Fast
Screw Speed	60 to 150	rpm