| Reny® 1501AH | |||
| Polyarylamide | |||
| 30% Glass Fiber | |||
| Product Description | |||
| Reny® 1501AH is a Polyarylamide (PARA) material filled with 30% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. | |||
| Important attributes of Reny® 1501AH are: | |||
| Flame Rated | |||
| Flame Retardant | |||
| General | |||
| Filler / Reinforcement | Glass Fiber, 30% Filler by Weight | ||
| Additive | Flame Retardant | ||
| Features | Flame Retardant | ||
| Processing Method | Injection Molding | ||
| Physical | Dry | Conditioned | Unit | Test Method |
| Density | 1.56 | -- | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (275°C/2.16 kg) | 20 | -- | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (275°C/2.16 kg) | 13.8 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.57 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 0.19 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.2 | -- | % | |
| Mechanical | Dry | Conditioned | Unit | Test Method |
| Tensile Modulus | 13300 | 11700 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 162 | 135 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.6 | 1.6 | % | ISO 527-2 |
| Flexural Modulus | 12100 | 11800 | MPa | ISO 178 |
| Flexural Stress | 251 | 222 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
| Charpy Notched Impact Strength (23°C) | 5.3 | 5.5 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 37 | 29 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 237 | 232 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 220 | 211 | °C | ISO 75-2/A |
| CLTE | ISO 11359-2 | |||
| Flow | 2.00E-05 | -- | cm/cm/°C | |
| Transverse | 5.00E-05 | -- | cm/cm/°C | |
| Electrical | Dry | Conditioned | Unit | Test Method |
| Surface Resistivity | 8.00E+14 | 4.00E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.00E+16 | 1.00E+15 | ohms·cm | IEC 60093 |
| Electric Strength | IEC 60243-1 | |||
| 1.00 mm | 29 | 26 | kV/mm | |
| 2.00 mm | 22 | 19 | kV/mm | |
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | -- | 5 | ||
| 1 MHz | -- | 4 | ||
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | -- | 0.016 | ||
| 1 MHz | -- | 0.014 | ||
| Comparative Tracking Index | 450 | 400 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
| Flame Rating (1.60 mm) | V-0 | -- | UL 94 | |
| Injection | Dry | Unit | ||
| Drying Temperature | ||||
| A | 120 | °C | ||
| B | 80 | °C | ||
| Drying Time | ||||
| A | > 3.0 | hr | ||
| B | > 12 | hr | ||
| Rear Temperature | 260 | °C | ||
| Middle Temperature | 265 | °C | ||
| Front Temperature | 270 | °C | ||
| Nozzle Temperature | 270 | °C | ||
| Mold Temperature | 120 to 145 | °C | ||
| Injection Pressure | 20.0 to 150 | MPa | ||
| Injection Rate | Moderate-Fast | |||
| Screw Speed | 60 to 150 | rpm |