Stanyl® ForTii™ LED LXPolyamide 4T
Glass Fiber
DSM Engineering Plastics
Product Description:
Stanyl® ForTii™ LED LX is a Polyamide 4T (Nylon 4T) material filled with glass fiber. It is available in Asia Pacific, Europe, or North America. Primary attribute of Stanyl® ForTii™ LED LX: Flame Rated.
|
General
|
|||
| Filler / Reinforcement | Glass Fiber | ||
| Physical | Nominal Value | Unit | Test Method |
| Density | 1.77 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.8 | % | |
| Flow | 0.6 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.4 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
| Tensile Modulus | 10000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 100 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.2 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
| Charpy Notched Impact Strength (23°C) | 1.5 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 230 | °C | ISO 75-2/A |
| Melting Temperature 3 | 325 | °C | ISO 11357-3 |
| Flammability | Nominal Value | Test Method | |
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 0.750 mm | HB | ||
| 1.50 mm | HB | ||
| Injection | Nominal Value | Unit | |
| Drying Temperature | 100 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 320 to 330 | °C | |
| Middle Temperature | 325 to 335 | °C | |
| Front Temperature | 330 to 335 | °C | |
| Nozzle Temperature | 330 to 335 | °C | |
| Processing (Melt) Temp | 330 to 340 | °C | |
| Mold Temperature | 100 to 150 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.500 to 3.00 | MPa | |
| Screw Compression Ratio | 2.5:1.0 | ||