塑胶原料 > 产品分类 > PARA芳族聚酰胺

PARA Ixef® DW-1022

PARA Ixef® DW-1022

2020-07-21

Ixef® DW-1022      
聚丙烯酰胺      
50% 玻璃纤维增强材料      
产品说明
Ixef® DW-1022 is a 50% glass-fiber reinforced, general purpose polyarylamide compound that exhibits very high strength and rigidity, outstanding surface gloss, and excellent creep resistance.
 
Ixef® DW-1022 is approved for use in potable water in France, Germany, the United States and the United Kingdom.
 
Black: DW-1022 BK 000
 
Natural: DW-1022 NT 000
 
总体  
UL 黄卡 2  E95746-101887929
填料/增强材料  玻璃纤维增强材料, 50% 填料按重量
特性  超强刚性 高强度 耐化学性良好
　 　 　
尺寸稳定性良好 好的消毒性 通用
　 　 　
出色的外观 良好的抗蠕变性 　
　 　 　
低吸湿性 流动性高 　
　 　 　
用途  电器用具 医疗器材 　
　 　
高光应用 饮用水应用
　 　
机构评级  ACS 未评级 FDA 21 CFR 176.170， 表2，状态D KTW 未评级 3
　 　 　
DVGW W270 FDA 21 CFR 176.170， 表2，状态G NSF 61 4
　 　 　
FDA 21 CFR 176.170， 表 2，状态 C FDA 21 CFR 176.170，表2，状态F WRAS 未评级 at 85°C
　 　 　
FDA 21 CFR 176.170， 表2，状态 B FDA 21 CFR 176.170，表2，状态H 欧洲 No 10/2011
　 　 　
RoHS 合规性  RoHS 合规
外观  黑色 自然色 　
形式  粒子
加工方法  注射成型

物理性能 干燥 调节后的 单位制 测试方法
密度 1.64 -- g/cm³ ISO 1183
收缩率 0.10 到 0.30 -- % ISO 294-4
吸水率 (23°C, 24 hr) 0.16 -- % ISO 62
机械性能 干燥 调节后的 单位制 测试方法
拉伸模量 19500 19500 MPa ISO 527-2
拉伸应力 (断裂) 280 260 MPa ISO 527-2
拉伸应变 (断裂) 1.9 2.2 % ISO 527-2
弯曲模量 18500 -- MPa ISO 178
弯曲应力 380 -- MPa ISO 178
冲击性能 干燥 调节后的 单位制 测试方法
悬壁梁缺口冲击强度 110 -- J/m ASTM D256
无缺口悬臂梁冲击 850 -- J/m ASTM D256
热性能 干燥 调节后的 单位制 测试方法
热变形温度 (1.8 MPa, 未退火) 230 -- °C ISO 75-2/A
线形热膨胀系数 - 流动  1.50E-05 -- cm/cm/°C ISO 11359-2
补充信息 干燥 调节后的 　 　
吸水性 - Equil, 65% RH  -- 　 　 　
注射 干燥 单位制 　 　
干燥温度 120 °C 　 　
干燥时间 0.50 到 1.5 hr 　 　
料筒后部温度 250 到 260 °C 　 　
料筒前部温度 260 到 290 °C 　 　
射嘴温度 260 到 290 °C 　 　
加工（熔体）温度 280 °C 　 　
模具温度 120 到 140 °C 　 　
注射速度 快速 　 　 　
注射说明 　
Hot runners: 250°C to 260°C (482°C to 500°F) 　
　 　
Storage 　
Ixef® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Ixef® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Ixef® processing guide. 　
　 　
Drying 　
The material as supplied is ready for molding without drying. However, If the bags have been open for longer than 24 hours, the material needs to be dried. When using a desiccant air dryer with dew point of -28°C (-18°F) or lower, these guidelines can be followed: 0.5-1.5 hour at 120°C (248°F), 1-3 hours at 100°C (212°F), or 1-7 hours at 80°C (176°F). 　
　 　
Injection Molding 　
Ixef® DW-1022 compound can be readily injection molded in most screw injection molding machines. A general purpose screw is recommended, with minimum back pressure. 　
　 　
The measured melt temperature should be about 280°C (536°F), and the barrel temperatures should be around 250 to 260°C (482 to 500°F) in the rear zone, gradually increasing to 260 to 290°C (500 to 554°F) in the front zone. If hot runners are used, they should be set to 250 to 260°C (482 to 500°F). 　
　 　
To maximize crystallinity, the temperature of the mold cavity surface must be held between 120 and 140°C (248 and 284°F). Molding at lower temperatures will produce articles that may warp, have poor surface appearance, and have a greater tendency to creep. Set injection pressure to give rapid injection. Adjust holding pressure and hold time to maximize part weight. Transfer from injection to hold pressure at the screw position just before the part is completely filled (95-99%). 　
备注
1通过这些链接您能够访问供应商资料。我们尽量保证及时更新资料；不过您可以从供应商处了解最新资料。
2UL 黄卡含有 UL 验证的易燃性和电气特性。UL Prospector 持续努力在 Prospector 中将黄卡链接至单个塑料材料，然而此列表可能未包括所有相应链接。重要的是，我们对 Prospector 中找到的这些黄卡和塑料材料之间的关联进行验证。如需完整的黄卡列表，请访问 UL 黄卡搜索。
3up to 60°C simple fitting 80<DN<300mm
4at 60°C and 82°Cfor 275 sq inch/l, 23°C