PARA Reny® 2051DS

2018-09-05

Reny® 2051DS
Polyarylamide
20% Glass\Mineral

Product Description
Reny® 2051DS is a Polyarylamide (PARA) material filled with 20% glass\mineral. It is available in Asia Pacific, Europe, or North America for injection molding.

Important attributes of Reny® 2051DS are:

Flame Rated

Warp Resistant

General
UL Yellow Card²	E41179-538646

Filler / Reinforcement	Glass\Mineral, 20% Filler by Weight

Features	Low Warpage

Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Density	1.62	g/cm³	ISO 1183
Molding Shrinkage	0.52	%
Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	15800	MPa	ISO 527-2
Tensile Stress (Break)	192	MPa	ISO 527-2
Tensile Strain (Break)	1.7	%	ISO 527-2
Flexural Modulus	15100	MPa	ISO 178
Flexural Stress	312	MPa	ISO 178
Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	8	kJ/m²	ISO 179
Charpy Unnotched Impact Strength (23°C)	64	kJ/m²	ISO 179
Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	242	°C	ISO 75-2/A
CLTE			ISO 11359-2
Flow	2.00E-05	cm/cm/°C
Transverse	5.00E-05	cm/cm/°C
Flammability	Nominal Value		Test Method
Flame Rating	HB		UL 94
Injection	Nominal Value	Unit
Drying Temperature
A	120	°C
B	80	°C
Drying Time
A	> 3.0	hr
B	> 12	hr
Rear Temperature	280	°C
Middle Temperature	285	°C
Front Temperature	290	°C
Nozzle Temperature	290	°C
Mold Temperature	80.0 to 140	°C
Injection Pressure	20.0 to 150	MPa
Injection Rate	Moderate-Fast
Screw Speed	60 to 150	rpm