| Nylon-MXD6 K7007C | |||
| Polyarylamide | |||
| Product Description | |||
| Nylon-MXD6 K7007C is a Polyarylamide (PARA) product. It is available in Asia Pacific, Europe, or North America. Typical application: Food Contact Applications. | |||
| General | |||
| Agency Ratings | EU Food Contact, Unspecified Rating | ||
| Physical | Nominal Value | Unit | Test Method |
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Water Absorption (Equilibrium, 20°C, 65) | 5.8 | % | ASTM D570 |
| Moisture Regain 2 (20°C) | 3.1 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
| Rockwell Hardness (M-Scale) | 108 | ASTM D785 | |
| Mechanical | Nominal Value | Unit | Test Method |
| Tensile Modulus | 4700 | MPa | ASTM D638 |
| Tensile Strength | 99 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.3 | % | ASTM D638 |
| Flexural Modulus | 4400 | MPa | ASTM D790 |
| Flexural Strength | 160 | MPa | ASTM D790 |
| Films | Nominal Value | Unit | Test Method |
| Carbon Dioxide Transmission Rate (23°C, 60% RH) | 0.42 | cm³/m²/24 hr | |
| Oxygen Permeability | |||
| 23°C 3 | 0.11 | cm³/m²/24 hr | |
| 23°C 4 | 0.07 | cm³/m²/24 hr | |
| Water Vapor Transmission Rate (40°C, 90% RH) | 1.4 | g/m²/24 hr | |
| Impact | Nominal Value | Unit | Test Method |
| Notched Izod Impact | 20 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
| Glass Transition Temperature | 85 | °C | DSC |
| Melting Temperature | 237 | °C | DSC |
| CLTE - Flow | 5.00E-05 | cm/cm/°C | ASTM D696 |
| Heat Distortion | 96 | °C | ASTM D648 |
| Additional Information | Nominal Value | Unit | |
| Semi-Crystallization Time (160°C) | 1.5 | min | |
| Notes | |||
| 2Equilibrium, 65% relative humidity | |||
| 380%RH | |||
| 460%RH |