PARA Reny® 1021UCS

2018-09-05

Reny® 1021UCS
Polyarylamide
50% Glass Fiber
Product Description
Reny® 1021UCS is a Polyarylamide (PARA) material filled with 50% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Primary attribute of Reny® 1021UCS: Flame Rated.
General
Filler / Reinforcement	Glass Fiber, 50% Filler by Weight

Processing Method	Injection Molding

Physical	Dry	Conditioned	Unit	Test Method
Density	1.61	--	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (275°C/2.16 kg)	13	--	g/10 min	ISO 1133
Melt Volume-Flow Rate (MVR) (275°C/2.16 kg)	11.1	--	cm³/10min	ISO 1133
Molding Shrinkage	0.4	--	%
Water Absorption	ISO 62
Saturation, 23°C	0.47	--	%
Equilibrium, 23°C, 50% RH	1.3	--	%
Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus	17800	14400	MPa	ISO 527-2
Tensile Stress (Break)	252	184	MPa	ISO 527-2
Tensile Strain (Break)	2.5	3.4	%	ISO 527-2
Flexural Modulus	18300	13800	MPa	ISO 178
Flexural Stress	392	305	MPa	ISO 178
Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength (23°C)	14	16	kJ/m²	ISO 179
Charpy Unnotched Impact Strength (23°C)	87	100	kJ/m²	ISO 179
Thermal	Dry	Conditioned	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, Unannealed	227	221	°C	ISO 75-2/B
1.8 MPa, Unannealed	217	210	°C	ISO 75-2/A
Flammability	Dry	Conditioned	Test Method
Flame Rating	HB	--	UL 94
Injection	Dry	Unit
Drying Temperature
A	120	°C
B	80	°C
Drying Time
A	> 3.0	hr
B	> 12	hr
Rear Temperature	270	°C
Middle Temperature	275	°C
Front Temperature	280	°C
Nozzle Temperature	280	°C
Mold Temperature	120 to 140	°C
Injection Pressure	20.0 to 150	MPa
Injection Rate	Moderate-Fast
Screw Speed	60 to 150	rpm

：0.00元/