PARA Reny® 1002HUS

2018-09-05

Reny® 1002HUS
Polyarylamide
30% Glass Fiber
Product Description
Reny® 1002HUS is a Polyarylamide (PARA) material filled with 30% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding.

Important attributes of Reny® 1002HUS are:

Flame Rated

Good Weather Resistance

General
UL Yellow Card²	E41179-100052204

	E41179-100085133

Filler / Reinforcement	Glass Fiber, 30% Filler by Weight

Features	Good Weather Resistance

Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Density	1.49	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (275°C/2.16 kg)	7	g/10 min	ISO 1133
Melt Volume-Flow Rate (MVR) (275°C/2.16 kg)	5	cm³/10min	ISO 1133
Molding Shrinkage	0.35	%
Water Absorption (Equilibrium, 23°C, 50% RH)	1.5	%	ISO 62
Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	15000	MPa	ISO 527-2
Tensile Stress (Break)	192	MPa	ISO 527-2
Tensile Strain (Break)	1.4	%	ISO 527-2
Flexural Modulus	13100	MPa	ISO 178
Flexural Stress	308	MPa	ISO 178
Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	7	kJ/m²	ISO 179
Charpy Unnotched Impact Strength (23°C)	48	kJ/m²	ISO 179
Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	237	°C	ISO 75-2/A
Flammability	Nominal Value	Test Method
Flame Rating	HB	UL 94
Injection	Nominal Value	Unit
Drying Temperature
A	120	°C
B	80	°C
Drying Time
A	> 3.0	hr
B	> 12	hr
Rear Temperature	280	°C
Middle Temperature	285	°C
Front Temperature	290	°C
Nozzle Temperature	290	°C
Mold Temperature	80.0 to 140	°C
Injection Pressure	20.0 to 150	MPa
Injection Rate	Moderate-Fast
Screw Speed	60 to 150	rpm