Reny® 1035
Polyarylamide
60% Glass Fiber
Product Description
Reny® 1035 is a Polyarylamide (PARA) material filled with 60% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding.

Important attributes of Reny® 1035 are:

Flame Rated

High Strength

General
Filler / Reinforcement	Glass Fiber, 60% Filler by Weight

Features	High Strength

Processing Method	Injection Molding

Physical	Dry	Conditioned	Unit	Test Method
Density	1.67	--	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (275°C/2.16 kg)	3.8	--	g/10 min	ISO 1133
Melt Volume-Flow Rate (MVR) (275°C/2.16 kg)	2.3	--	cm³/10min	ISO 1133
Molding Shrinkage	0.26	--	%
Water Absorption				ISO 62
Saturation, 23°C	0.12	--	%
Equilibrium, 23°C, 50% RH	0.9	--	%
Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus	24300	23400	MPa	ISO 527-2
Tensile Stress (Break)	285	250	MPa	ISO 527-2
Tensile Strain (Break)	1.6	1.7	%	ISO 527-2
Flexural Modulus	21600	20000	MPa	ISO 178
Flexural Stress	447	407	MPa	ISO 178
Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength (23°C)	20	15	kJ/m²	ISO 179
Charpy Unnotched Impact Strength (23°C)	80	82	kJ/m²	ISO 179
Thermal	Dry	Conditioned	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, Unannealed	240	233	°C	ISO 75-2/B
1.8 MPa, Unannealed	232	225	°C	ISO 75-2/A
CLTE				ISO 11359-2
Flow	1.00E-05	--	cm/cm/°C
Transverse	4.00E-05	--	cm/cm/°C
Flammability	Dry	Conditioned		Test Method
Flame Rating	HB	--		UL 94
Injection	Dry	Unit
Drying Temperature
A	120	°C
B	80	°C
Drying Time
A	> 3.0	hr
B	> 12	hr
Rear Temperature	270	°C
Middle Temperature	275	°C
Front Temperature	280	°C
Nozzle Temperature	280	°C
Mold Temperature	120 to 140	°C
Injection Pressure	20.0 to 150	MPa
Injection Rate	Moderate-Fast
Screw Speed	60 to 150	rpm