PARA Reny® 1507

2018-09-05

Reny® 1507
Polyarylamide
30% Glass Fiber
Product Description
Reny® 1507 is a Polyarylamide (PARA) material filled with 30% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding.

Important attributes of Reny® 1507 are:

Flame Rated

Flame Retardant

Halogen Free

General
UL Yellow Card²	E41179-100092029

Filler / Reinforcement	Glass Fiber, 30% Filler by Weight

Additive	Flame Retardant

Features	Flame Retardant	Halogen Free

Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Density	1.51	g/cm³	ISO 1183
Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	12500	MPa	ISO 527-2
Tensile Stress (Break)	169	MPa	ISO 527-2
Tensile Strain (Break)	1.8	%	ISO 527-2
Flexural Modulus	12000	MPa	ISO 178
Flexural Stress	288	MPa	ISO 178
Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	7.8	kJ/m²	ISO 179
Charpy Unnotched Impact Strength (23°C)	52	kJ/m²	ISO 179
Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	222	°C	ISO 75-2/A
Electrical	Nominal Value	Unit	Test Method
Comparative Tracking Index	325	V	IEC 60112
Flammability	Nominal Value	Unit	Test Method
Flame Rating (1.60 mm)	V-0		UL 94
Injection	Nominal Value	Unit
Drying Temperature
A	120	°C
B	80	°C
Drying Time
A	> 3.0	hr
B	> 12	hr
Rear Temperature	260	°C
Middle Temperature	265	°C
Front Temperature	270	°C
Nozzle Temperature	270	°C
Mold Temperature	120 to 145	°C
Injection Pressure	20.0 to 150	MPa
Injection Rate	Moderate-Fast
Screw Speed	60 to 150	rpm