| Reny® 4511 | |||
| Polyarylamide | |||
| 40% Glass Fiber | |||
| Product Description | |||
| Reny® 4511 is a Polyarylamide (PARA) material filled with 40% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. | |||
| Important attributes of Reny® 4511 are: | |||
| Flame Rated | |||
| Flame Retardant | |||
| Conductive | |||
| General | |||
| UL Yellow Card 2 | E41179-231773 | ||
| Filler / Reinforcement | Glass Fiber, 40% Filler by Weight | ||
| Additive | Flame Retardant | ||
| Features | Electrically Conductive | Flame Retardant | |
| Processing Method | Injection Molding | ||
| Physical | Dry | Conditioned | Unit | Test Method |
| Density | 1.77 | -- | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (280°C/3.8 kg) | 1.8 | -- | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (280°C/3.8 kg) | 1 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.35 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 0.06 | -- | % | |
| Equilibrium, 23°C, 50% RH | 0.7 | -- | % | |
| Mechanical | Dry | Conditioned | Unit | Test Method |
| Tensile Modulus | 20900 | 20600 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 130 | 125 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 0.6 | 0.8 | % | ISO 527-2 |
| Flexural Modulus | 22200 | 22000 | MPa | ISO 178 |
| Flexural Stress | 215 | 208 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
| Charpy Notched Impact Strength (23°C) | 6.9 | 8.9 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 12 | 12 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 234 | 232 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 223 | 218 | °C | ISO 75-2/A |
| CLTE | ISO 11359-2 | |||
| Flow | 8.00E-06 | -- | cm/cm/°C | |
| Transverse | 4.00E-05 | -- | cm/cm/°C | |
| Electrical | Dry | Conditioned | Unit | Test Method |
| Surface Resistivity | 5.00E+03 | 4.00E+04 | ohms | IEC 60093 |
| Volume Resistivity | 3.00E+02 | 7.00E+08 | ohms·cm | IEC 60093 |
| Flammability | Dry | Conditioned | Unit | Test Method |
| Flame Rating (1.60 mm) | V-0 | -- | UL 94 | |
| Injection | Dry | Unit | ||
| Drying Temperature | ||||
| A | 120 | °C | ||
| B | 80 | °C | ||
| Drying Time | ||||
| A | > 3.0 | hr | ||
| B | > 12 | hr | ||
| Rear Temperature | 260 | °C | ||
| Middle Temperature | 265 | °C | ||
| Front Temperature | 270 | °C | ||
| Nozzle Temperature | 270 | °C | ||
| Mold Temperature | 120 to 140 | °C | ||
| Injection Pressure | 20.0 to 150 | MPa | ||
| Injection Rate | Moderate-Fast | |||
| Screw Speed | 60 to 150 | rpm |