PARA Reny® 2505

2018-09-05

Reny® 2505
Polyarylamide
15% Glass\Mineral
Product Description
Reny® 2505 is a Polyarylamide (PARA) material filled with 15% glass\mineral. It is available in Asia Pacific, Europe, or North America for injection molding.

Important attributes of Reny® 2505 are:

Flame Rated

Flame Retardant

General
UL Yellow Card²	E41179-231762

Filler / Reinforcement	Glass\Mineral, 15% Filler by Weight

Additive	Flame Retardant

Features	Flame Retardant

Processing Method	Injection Molding

Physical	Dry	Conditioned	Unit	Test Method
Density	1.81	--	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (275°C/2.16 kg)	11	--	g/10 min	ISO 1133
Melt Volume-Flow Rate (MVR) (275°C/2.16 kg)	6.2	--	cm³/10min	ISO 1133
Molding Shrinkage	0.43	--	%
Water Absorption				ISO 62
Saturation, 23°C	0.13	--	%
Equilibrium, 23°C, 50% RH	0.7	--	%
Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus	13900	13600	MPa	ISO 527-2
Tensile Stress (Break)	124	109	MPa	ISO 527-2
Tensile Strain (Break)	1.2	1.1	%	ISO 527-2
Flexural Modulus	13600	12900	MPa	ISO 178
Flexural Stress	200	176	MPa	ISO 178
Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength (23°C)	3.2	3	kJ/m²	ISO 179
Charpy Unnotched Impact Strength (23°C)	25	20	kJ/m²	ISO 179
Thermal	Dry	Conditioned	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, Unannealed	236	231	°C	ISO 75-2/B
1.8 MPa, Unannealed	215	205	°C	ISO 75-2/A
Electrical	Dry	Conditioned	Unit	Test Method
Comparative Tracking Index	> 600	--	V	IEC 60112
Flammability	Dry	Conditioned	Unit	Test Method
Flame Rating (1.60 mm)	V-0	--		UL 94
Injection	Dry	Unit
Drying Temperature
A	120	°C
B	80	°C
Drying Time
A	> 3.0	hr
B	> 12	hr
Rear Temperature	270	°C
Middle Temperature	275	°C
Front Temperature	280	°C
Nozzle Temperature	280	°C
Mold Temperature	120 to 145	°C
Injection Pressure	20.0 to 150	MPa
Injection Rate	Moderate-Fast
Screw Speed	60 to 150	rpm