PARA Reny® 2686
2018-09-05
Reny® 2686 |
|
|
|
Polyarylamide |
|
|
|
65% Glass Bead |
|
|
|
Product Description |
Reny® 2686 is a Polyarylamide (PARA) material filled with 65% glass bead. It is available in Asia Pacific, Europe, or North America for injection molding. Primary attribute of Reny® 2686: Warp Resistant. |
General |
|
Filler / Reinforcement |
Glass Bead, 65% Filler by Weight |
Features |
Low Warpage |
Processing Method |
Injection Molding |
Physical |
Dry |
Conditioned |
Unit |
Test Method |
Density |
1.8 |
-- |
g/cm³ |
ISO 1183 |
Melt Mass-Flow Rate (MFR) (275°C/2.16 kg) |
7.6 |
-- |
g/10 min |
ISO 1133 |
Melt Volume-Flow Rate (MVR) (275°C/2.16 kg) |
6.9 |
-- |
cm³/10min |
ISO 1133 |
Molding Shrinkage |
0.87 |
-- |
% |
|
Water Absorption |
|
|
|
ISO 62 |
Saturation, 23°C |
0.11 |
-- |
% |
|
Equilibrium, 23°C, 50% RH |
0.7 |
-- |
% |
|
Mechanical |
Dry |
Conditioned |
Unit |
Test Method |
Tensile Modulus |
9800 |
7300 |
MPa |
ISO 527-2 |
Tensile Stress (Break) |
73 |
52 |
MPa |
ISO 527-2 |
Tensile Strain (Break) |
1.7 |
1.8 |
% |
ISO 527-2 |
Flexural Modulus |
9600 |
6600 |
MPa |
ISO 178 |
Flexural Stress |
147 |
103 |
MPa |
ISO 178 |
Impact |
Dry |
Conditioned |
Unit |
Test Method |
Charpy Notched Impact Strength (23°C) |
2.2 |
2.4 |
kJ/m² |
ISO 179 |
Charpy Unnotched Impact Strength (23°C) |
32 |
40 |
kJ/m² |
ISO 179 |
Thermal |
Dry |
Conditioned |
Unit |
Test Method |
Heat Deflection Temperature |
|
|
|
|
0.45 MPa, Unannealed |
213 |
207 |
°C |
ISO 75-2/B |
1.8 MPa, Unannealed |
147 |
116 |
°C |
ISO 75-2/A |
Injection |
Dry |
Unit |
|
|
Drying Temperature |
|
|
|
|
A |
120 |
°C |
|
|
B |
80 |
°C |
|
|
Drying Time |
|
|
|
|
A |
> 3.0 |
hr |
|
|
B |
> 12 |
hr |
|
|
Rear Temperature |
270 |
°C |
|
|
Middle Temperature |
275 |
°C |
|
|
Front Temperature |
280 |
°C |
|
|
Nozzle Temperature |
280 |
°C |
|
|
Mold Temperature |
120 to 140 |
°C |
|
|
Injection Pressure |
20.0 to 150 |
MPa |
|
|
Injection Rate |
Moderate-Fast |
|
|
|
Screw Speed |
60 to 150 |
rpm |
|
|