PARA Reny® 1038

2018-09-05

Reny® 1038
Polyarylamide
60% Long Glass Fiber
Product Description
Reny® 1038 is a Polyarylamide (PARA) material filled with 60% long glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Primary attribute of Reny® 1038: Flame Rated.
General
Material Status	Commercial: Active


Filler / Reinforcement	Long Glass Fiber, 60% Filler by Weight

Processing Method	Injection Molding

Physical	Dry	Conditioned	Unit	Test Method
Density	1.76	--	g/cm³	ISO 1183
Molding Shrinkage	0.41	--	%
Water Absorption				ISO 62
Saturation, 23°C	0.1	--	%
Equilibrium, 23°C, 50% RH	1.8	--	%
Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus	26700	21300	MPa	ISO 527-2
Tensile Stress (Break)	262	259	MPa	ISO 527-2
Tensile Strain (Break)	1.3	1.6	%	ISO 527-2
Flexural Modulus	24000	23000	MPa	ISO 178
Flexural Stress	477	409	MPa	ISO 178
Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength (23°C)	35	36	kJ/m²	ISO 179
Charpy Unnotched Impact Strength (23°C)	70	86	kJ/m²	ISO 179
Thermal	Dry	Conditioned	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, Unannealed	239	236	°C	ISO 75-2/B
1.8 MPa, Unannealed	234	227	°C	ISO 75-2/A
Flammability	Dry	Conditioned		Test Method
Flame Rating	HB	--		UL 94
Injection	Dry	Unit
Drying Temperature
A	120	°C
B	80	°C
Drying Time
A	> 3.0	hr
B	> 12	hr
Rear Temperature	270	°C
Middle Temperature	275	°C
Front Temperature	280	°C
Nozzle Temperature	280	°C
Mold Temperature	120 to 140	°C
Injection Pressure	20.0 to 150	MPa
Injection Rate	Moderate-Fast
Screw Speed	60 to 150	rpm